Celanese Corporation塞拉尼斯PPS，玻璃纤维增强材料，NSF饮用水接触许可, 阻燃

 

Fortron® 1140L4

聚苯硫醚

 

Celanese Corporation

 

Technical Data

 

产品说明

40% Glass reinforced, strong and tough, V-0

Fortron 1140L4 is a 40% glass-reinforced grade that is the strongest and toughest product available. It exhibits excellent heat and chemical resistance, good electrical properties and is inherently flame-retardant. The high hardness and rigidity at elevated temperatures allows for good load bearing performance. This product has good weldability due to the modest filler level. Applications made of this grade are electronical components (i.e. bobbins, lamp housings, brush holders) and various other components requiring strength and resistance to aggressive chemicals (i.e. automotive heaters, pumps, valves, fuel rails, microwave oven rings and distillation column packings).

总览

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

•  E107854-237738

UL 黄卡 2 •  E107854-237739

• E107854-237735

搜索 UL 黄卡 •  Celanese Corporation

•  Fortron®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

填料/增强材料 • 玻璃纤维增强材料

添加剂 • 脱模 • 阻燃性

特性 • 饮用水接触许可 • 阻燃性

用途 • 汽车领域的应用

形式 • 粒子

加工方法 • 注射成型

• Creep Modulus vs. Time (ISO 11403-1)

• Isochronous Stress vs. Strain (ISO 11403-1)

多点数据 • Isothermal Stress vs. Strain (ISO 11403-1)

• Secant Modulus vs. Strain (ISO 11403-1)

• Shear Modulus vs. Temperature, Dynamic (ISO 11403-1)

• Specific Volume vs Temperature (ISO 11403-2)

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 1.65g/cm³ 1.65g/cm³ ISO 1183

表观密度 0.72g/cm³ 0.72g/cm³ ISO 60

收缩率 ISO 294-4

垂直 0.60% 0.60%

流动 0.30% 0.30%

吸水率 (饱和, 73°F (23°C)) 0.020% 0.020% ISO 62

机械性能 额定值(英制) 额定值(公制) 测试方法

拉伸模量 2.13E+6psi 14700MPa ISO 527-1

拉伸应力 (断裂) 28300psi 195MPa ISO 527-2/5

拉伸应变 (断裂) 1.8% 1.8% ISO 527-2/5

弯曲模量 (73°F (23°C)) 2.10E+6psi 14500MPa ISO 178

弯曲应力 4 41300psi 285MPa ISO 178

压缩模量 2.18E+6psi 15000MPa ISO 604

 

Fortron® 1140L4

聚苯硫醚

 

Celanese Corporation

冲击性能 额定值(英制) 额定值(公制) 测试方法

简支梁缺口冲击强度 ISO 179/1eA

-22°F (-30°C) 4.8ft•lb/in² 10kJ/m²

73°F (23°C) 4.8ft•lb/in² 10kJ/m²

简支梁无缺口冲击强度 ISO 179/1eU

-22°F (-30°C) 25ft•lb/in² 53kJ/m²

73°F (23°C) 25ft•lb/in² 53kJ/m²

悬壁梁缺口冲击强度 ISO 180/1A

-22°F (-30°C) 4.8ft•lb/in² 10kJ/m²

73°F (23°C) 4.8ft•lb/in² 10kJ/m²

无缺口伊佐德冲击强度 ISO 180/1U

-22°F (-30°C) 16ft•lb/in² 34kJ/m²

73°F (23°C) 16ft•lb/in² 34kJ/m²

硬度 额定值(英制) 额定值(公制) 测试方法

洛氏硬度 (M 计秤) 100 100 ISO 2039-2

热性能 额定值(英制) 额定值(公制) 测试方法

载荷下热变形温度

264 psi (1.8 MPa), 未退火 518°F 270°C ISO 75-2/A

1160 psi (8.0 MPa), 未退火 419°F 215°C ISO 75-2/C

玻璃转化温度 5 194°F 90.0°C ISO 11357-2

Ball Pressure Test (500°F (260°C)) 通过 通过 IEC 60695-10-2

熔融温度 5 536°F 280°C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 1.4E-5in/in/°F 2.6E-5cm/cm/°C

垂直 2.3E-5in/in/°F 4.2E-5cm/cm/°C

电气性能 额定值(英制) 额定值(公制) 测试方法

表面电阻率 IEC 62631-3-2

73°F (23°C) > 1.0E+17ohms > 1.0E+17ohms

428°F (220°C) > 1.0E+12ohms > 1.0E+12ohms

体积电阻率 IEC 62631-3-1

73°F (23°C) > 1.0E+15ohms•m > 1.0E+15ohms•m

428°F (220°C) > 1.0E+13ohms•m > 1.0E+13ohms•m

介电强度 IEC 60243-1

73°F (23°C) 6 790V/mil 31kV/mm

73°F (23°C) 7 1000V/mil 40kV/mm

428°F (220°C) 6 580V/mil 23kV/mm

428°F (220°C) 7 790V/mil 31kV/mm

介电常数 (1 MHz) 4.10 4.10 IEC 60250

耗散因数 (1 MHz) 2.0E-3 2.0E-3 IEC 60250

相比耐漏电起痕指数(CTI) PLC 4 PLC 4 UL 746A

可燃性 额定值(英制) 额定值(公制) 测试方法

UL 阻燃等级 UL 94

0.015 in (0.38 mm) V-0 V-0

0.06 in (1.6 mm) V-0 V-0

0.12 in (3.0 mm) 5VA 5VA

灼热丝易燃指数 (0.016 in (0.40 mm)) 1760°F 960°C IEC 60695-2-12

热灯丝点火温度 IEC 60695-2-13

0.016 in (0.40 mm) 1520°F 825°C

0.031 in (0.8 mm) 1520°F 825°C

极限氧指数 47% 47% ISO 4589-2

充模分析 额定值(英制) 额定值(公制) 测试方法

熔体比热 0.359Btu/lb/°F 1500J/kg/°C 内部方法

 

Fortron® 1140L4

聚苯硫醚

 

Celanese Corporation

补充信息 额定值(英制) 额定值(公制) 测试方法

Specimen Thickness - shrinkage 0.13in 3.18mm 内部方法

注射 额定值(英制) 额定值(公制)

干燥温度 266 到 284°F 130 到 140°C

干燥时间 3.0 到 4.0hr 3.0 到 4.0hr

建议的最大水分含量 0.020% 0.020%

料斗温度 68 到 86°F 20 到 30°C

Injection Feed Temperature 140 到 176°F 60 到 80°C

料筒后部温度 554 到 572°F 290 到 300°C

料筒中部温度 590 到 608°F 310 到 320°C

料筒前部温度 626 到 644°F 330 到 340°C

Injection Zone 4 Temperature 626 到 644°F 330 到 340°C

射嘴温度 590 到 626°F 310 到 330°C

加工（熔体）温度 626°F 330°C

模具温度 284 到 320°F 140 到 160°C

注射速度 快速 快速

背压 < 435psi < 3.00MPa

Hot Runner 626 到 644°F 330 到 340°C

Screw Speed

0.98 in (2.50 cm) 120 120

1.6 in (4.00 cm) 75 75

2.2 in (5.50 cm) 50 50

 

 

 