Celanese Corporation塞拉尼斯PP，玻璃纤维增强材料, 低挥发, 流动性高

 

Celstran® PP-GF60-0453 HF Black

聚丙烯

Celanese Corporation

Technical Data

 

产品说明

Material code according to ISO 1043-1: PP Polypropylene with 60 weight percent ash content, long glass fibers reinforced, low emission. Concentrate, black. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 11 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive.

总览

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

搜索 UL 黄卡 •  Celanese Corporation

•  Celstran®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

填料/增强材料 • 玻璃纤维增强材料

特性 • 低挥发 • 流动性高 • 耐热性，良好

用途 • 色母料

形式 • 粒子

加工方法 • 注射成型

多点数据 • Isothermal Stress vs. Strain • Secant Modulus vs. Strain (ISO

(ISO 11403-1) 11403-1)

物理性能 额定值单位制 测试方法

密度 1.43g/cm³ ISO 1183

机械性能 额定值单位制 测试方法

拉伸模量 14700MPa ISO 527-1

拉伸应力 (断裂) 135MPa ISO 527-2/5

拉伸应变 (断裂) 1.2% ISO 527-2/5

弯曲模量 ISO 178

23°C 14300MPa

80°C 10700MPa

弯曲应力 ISO 178

23°C 255MPa

80°C 141MPa

冲击性能 额定值单位制 测试方法

简支梁缺口冲击强度 ISO 179/1eA

-30°C 35kJ/m²

23°C 41kJ/m²

简支梁无缺口冲击强度 ISO 179/1eU

-30°C 80kJ/m²

23°C 68kJ/m²

热性能 额定值单位制 测试方法

载荷下热变形温度 (1.8 MPa, 未退火) 151°C ISO 75-2/A

熔融温度 3 168°C ISO 11357-3

补充信息 额定值单位制 测试方法

Emission of Organic Compounds 30.0µgC/g VDA 277

Odor 3.50 VDA 270

Thermal Desorption Analysis of Organic Emissions 115GHz VDA 278

注射 额定值单位制

干燥温度 90 到 100°C

干燥时间 2.0hr

 

Celstran® PP-GF60-0453 HF Black

聚丙烯

 

Celanese Corporation

注射 额定值单位制

建议的最大水分含量 0.20%

Injection Feed Temperature 20 到 50°C

料筒后部温度 220 到 240°C

料筒中部温度 230 到 240°C

料筒前部温度 240 到 250°C

Injection Zone 4 Temperature 240 到 260°C

射嘴温度 240 到 260°C

加工（熔体）温度 230 到 260°C

模具温度 30 到 70°C

注射速度 慢

背压 < 3.00MPa

Hot Runner 230 到 270°C

Screw Speed

4.00 cm 50

5.50 cm 35

7.50 cm 25

 

 

 

 

塞拉尼斯聚丙烯PP,塞拉尼斯PP Celstran® PP-GF60-0453 HF Black是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123   13549213581 肖生    QQ：15397858   微信：13549213581