Celanese Corporation塞拉尼斯POM, 挤出

 

Hostaform® C 9021 AW

聚甲醛（POM）共聚物

Celanese Corporation

Technical Data

 

产品说明

Injection molding type like C 9021, with special additive modified

Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNS, 03-002 POM copolymer Injection molding type like C 9021, with special additive modified; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation; good wear properties and low coefficient of friction. UL-registration in natural and black and a thickness more than 1.5 mm as UL 94 HB. Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm. Ranges of applications: sliding parts for window lifter. UL = Underwriters Laboratories (USA) FMVSS = Federal Motor Vehicle Safety Standard (USA)

总览

材料状态 • 已商用：当前有效

UL 黄卡 1 • E42337-234611

搜索 UL 黄卡 •  Celanese Corporation

•  Hostaform®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

添加剂 • 润滑剂 • 脱模

特性 • 润滑

用途 • 汽车领域的应用

形式 • 粒子

加工方法 • 挤出 • 注射成型

多点数据 • Isothermal Stress vs. Strain • Secant Modulus vs. Strain (ISO • Specific Volume vs

(ISO 11403-1) 11403-1) Temperature (ISO 11403-2)

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 1.38g/cm³ 1.38g/cm³ ISO 1183

熔融体积流量（MVR） (190°C/2.16 kg) 8.0cm³/10min 8.0cm³/10min ISO 1133

收缩率 ISO 294-4

垂直 1.9% 1.9%

流动 2.1% 2.1%

吸水率 ISO 62

饱和, 73°F (23°C) 0.65% 0.65%

平衡, 73°F (23°C), 50% RH 0.20% 0.20%

机械性能 额定值(英制) 额定值(公制) 测试方法

拉伸模量 377000psi 2600MPa ISO 527-1/1A

拉伸应力 (屈服) 8410psi 58.0MPa ISO 527-2/1A/50

拉伸应变 (屈服) 8.0% 8.0% ISO 527-2/1A/50

标称拉伸断裂应变 20% 20% ISO 527-2/1A/50

拉伸蠕变模量 ISO 899-1

1 hr 334000psi 2300MPa

1000 hr 174000psi 1200MPa

冲击性能 额定值(英制) 额定值(公制) 测试方法

简支梁缺口冲击强度 ISO 179/1eA

-22°F (-30°C) 2.4ft•lb/in² 5.0kJ/m²

73°F (23°C) 2.9ft•lb/in² 6.0kJ/m²

简支梁无缺口冲击强度 ISO 179/1eU

-22°F (-30°C) 62ft•lb/in² 130kJ/m²

73°F (23°C) 71ft•lb/in² 150kJ/m²

硬度 额定值(英制) 额定值(公制) 测试方法

球压硬度 3 20300psi 140MPa ISO 2039-1

 

Hostaform® C 9021 AW

聚甲醛（POM）共聚物

 

Celanese Corporation

热性能 额定值(英制) 额定值(公制) 测试方法

热变形温度 (264 psi (1.8 MPa), 未退火) 190°F 88.0°C ISO 75-2/A

熔融温度 4 331°F 166°C ISO 11357-3

线形热膨胀系数 - 流动 6.1E-5in/in/°F 1.1E-4cm/cm/°C ISO 11359-2

电气性能 额定值(英制) 额定值(公制) 测试方法

表面电阻率 1.0E+14ohms 1.0E+14ohms IEC 60093

体积电阻率 1.0E+14ohms•cm 1.0E+14ohms•cm IEC 60093

介电强度 890V/mil 35kV/mm IEC 60243-1

介电常数 IEC 60250

100 Hz 3.80 3.80

1 MHz 3.80 3.80

耗散因数 IEC 60250

100 Hz 2.0E-3 2.0E-3

1 MHz 5.0E-3 5.0E-3

相比耐漏电起痕指数(CTI) PLC 0 PLC 0 UL 746A

可燃性 额定值(英制) 额定值(公制) 测试方法

UL 阻燃等级 UL 94

0.06 in (1.6 mm) HB HB

0.12 in (3.0 mm) HB HB

注射 额定值(英制) 额定值(公制)

干燥温度 212 到 248°F 100 到 120°C

干燥时间 3.0 到 4.0hr 3.0 到 4.0hr

建议的最大水分含量 0.15% 0.15%

料斗温度 68 到 86°F 20 到 30°C

Injection Feed Temperature 140 到 176°F 60 到 80°C

料筒后部温度 338 到 356°F 170 到 180°C

料筒中部温度 356 到 374°F 180 到 190°C

料筒前部温度 374 到 392°F 190 到 200°C

Injection Zone 4 Temperature 374 到 410°F 190 到 210°C

射嘴温度 374 到 410°F 190 到 210°C

加工（熔体）温度 374 到 410°F 190 到 210°C

模具温度 176 到 248°F 80 到 120°C

注射速度 慢 慢

背压 < 290psi < 2.00MPa

Hot Runner 374 到 410°F 190 到 210°C

Screw Speed

0.98 in (2.50 cm) 150 150

1.6 in (4.00 cm) 100 100

2.2 in (5.50 cm) 70 70

 

 

 

塞拉尼斯聚甲醛(POM),塞拉尼斯POM Hostaform® C 9021 AW是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123   13549213581 肖生    QQ：15397858   微信：13549213581