Hostaform® C 9021 GV1/20

聚甲醛（POM）共聚物

Celanese Corporation

Technical Data

 

产品说明

Injection molding grade, reinforced with ca. 20 % glass fibers

Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNR, 02-003, GF20 POM copolymer Injection molding type, reinforced with ca. 20 % glass fibers; high resistance to thermal and oxidative degradation; reduced thermal expansion and shrinkage. UL-registration in natural and black and a thickness more than 1.5 mm as UL 94 HB, temperature index UL 746 B, electrical 105 °C, mechanical 105 °C Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm thickness. Ranges of applications: For molded parts with high strength and rigidity as well as higher hardness. FMVSS = Federal Motor Vehicle Safety Standard (USA) UL = Underwriters Laboratories (USA)

总览

材料状态 • 已商用：当前有效

UL 黄卡 1 • E42337-234613

搜索 UL 黄卡 •  Celanese Corporation

•  Hostaform®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

填料/增强材料 • 玻璃纤维增强材料

添加剂 • 脱模

特性 • 饮用水接触许可

用途 • 汽车领域的应用

形式 • 粒子

加工方法 • 注射成型

• Isothermal Stress vs. Strain (ISO 11403-1)

多点数据 • Secant Modulus vs. Strain (ISO 11403-1)

• Shear Modulus vs. Temperature, Dynamic (ISO 11403-1)

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 1.55g/cm³ 1.55g/cm³ ISO 1183

熔融体积流量（MVR） (190°C/2.16 kg) 4.5cm³/10min 4.5cm³/10min ISO 1133

收缩率 ISO 294-4

垂直 1.1% 1.1%

流动 0.70% 0.70%

吸水率 ISO 62

饱和, 73°F (23°C) 0.85% 0.85%

平衡, 73°F (23°C), 50% RH 0.19% 0.19%

机械性能 额定值(英制) 额定值(公制) 测试方法

拉伸模量 1.04E+6psi 7200MPa ISO 527-1/1A

拉伸应力 (断裂) 17400psi 120MPa ISO 527-2/1A/5

拉伸应变 (断裂) 3.0% 3.0% ISO 527-2/1A/5

拉伸蠕变模量 ISO 899-1

1 hr 943000psi 6500MPa

1000 hr 580000psi 4000MPa

弯曲模量 (73°F (23°C)) 1.00E+6psi 6900MPa ISO 178

弯曲应力 3 24700psi 170MPa ISO 178

泊松比 0.43 0.43 ISO 527

断裂弯曲应变 3.4% 3.4% ISO 178

冲击性能 额定值(英制) 额定值(公制) 测试方法

简支梁缺口冲击强度 ISO 179/1eA

-22°F (-30°C) 3.8ft•lb/in² 8.0kJ/m²

73°F (23°C) 3.8ft•lb/in² 8.0kJ/m²

简支梁无缺口冲击强度 ISO 179/1eU

-22°F (-30°C) 19ft•lb/in² 40kJ/m²

73°F (23°C) 17ft•lb/in² 35kJ/m²

 

Hostaform® C 9021 GV1/20

聚甲醛（POM）共聚物

 

Celanese Corporation

硬度 额定值(英制) 额定值(公制) 测试方法

球压硬度 4 27600psi 190MPa ISO 2039-1

热性能 额定值(英制) 额定值(公制) 测试方法

热变形温度

264 psi (1.8 MPa), 未退火 318°F 159°C ISO 75-2/A

1160 psi (8.0 MPa), 未退火 221°F 105°C ISO 75-2/C

熔融温度 5 331°F 166°C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 2.8E-5in/in/°F 5.0E-5cm/cm/°C

垂直 4.4E-5in/in/°F 8.0E-5cm/cm/°C

电气性能 额定值(英制) 额定值(公制) 测试方法

表面电阻率 1.0E+14ohms 1.0E+14ohms IEC 60093

体积电阻率 1.0E+14ohms•cm 1.0E+14ohms•cm IEC 60093

介电强度 890V/mil 35kV/mm IEC 60243-1

介电常数 IEC 60250

100 Hz 4.30 4.30

1 MHz 4.30 4.30

耗散因数 IEC 60250

100 Hz 3.0E-3 3.0E-3

1 MHz 6.0E-3 6.0E-3

相比耐漏电起痕指数(CTI) PLC 0 PLC 0 UL 746A

可燃性 额定值(英制) 额定值(公制) 测试方法

UL 阻燃等级 UL 94

0.06 in (1.6 mm) HB HB

0.12 in (3.0 mm) HB HB

注射 额定值(英制) 额定值(公制)

干燥温度 212 到 248°F 100 到 120°C

干燥时间 3.0 到 4.0hr 3.0 到 4.0hr

建议的最大水分含量 0.15% 0.15%

料斗温度 68 到 86°F 20 到 30°C

Injection Feed Temperature 140 到 176°F 60 到 80°C

料筒后部温度 338 到 356°F 170 到 180°C

料筒中部温度 356 到 374°F 180 到 190°C

料筒前部温度 374 到 392°F 190 到 200°C

Injection Zone 4 Temperature 374 到 410°F 190 到 210°C

射嘴温度 374 到 410°F 190 到 210°C

加工（熔体）温度 374 到 410°F 190 到 210°C

模具温度 176 到 248°F 80 到 120°C

注射速度 慢 慢

背压 < 290psi < 2.00MPa

Hot Runner 374 到 410°F 190 到 210°C

Screw Speed

0.98 in (2.50 cm) 150 150

1.6 in (4.00 cm) 100 100

2.2 in (5.50 cm) 70 70

 

 

 